Ceramic Honeycomb Catalyst Honeycomb Ceramic Substrate (Used In Vehicle)

• Type: Catalytic Converter
• Body Material: Cordierite
• Discharge Standard: Euro IV
• Model NO.: Honeycomb Ceramic Catalyst Carrier
• Certification: ISO9001
• Component: Catalytic Converter
• Usage: Automotive Emission Catalytic Converter
• Transport Package: Wooden Box
• Specification: Customized
• Trademark: XINGFENG
• Origin: China
• HS Code: 6909110000
• Production Capacity: 5000 Cbm/Year

Product Description

Ceramic Honeycomb Catalyst Honeycomb Ceramic Substrate (Used In Vehicle)



Description:
The catalyst carrier is mainly used in the automotive and other high-temperature process exhaust. The main material is cordierite, after coated the catalyst, catalytic conversion of the exhaust, so as to achieve the national emission standards. It has characteristics of large surface area, small expansion coefficient, high strength, high water absorption, and good matching with the catalytic active component, heating up fast and
so on.

Characteristics:

1. Large specific surface area: to ensure full access to the exhaust gas with the catalyst;
2. Stable water absorption: to ensure the catalyst evenly firmly attached to the surface of the catalyst carrier;
3. Warm-up: after start-up the engine, the temperature of the carrier can reach the catalyst activation temperature in the shortest possible time;
4. Low exhaust resistance: the engine's exhaust resistance is small, to ensure that doesn't affect the engine performance;
5. High strength: the operating environment of the catalyst carrier is in the bumpy car, so the catalyst carrier must be high strength without being external damage;
6. Good assembly: the carrier is an exhaust assembly parts, only good appearance and precise dimensions can ensure perfect assembly.

Technical Data Sheet:

Name	index	Tolerance Range
Wall Thickness	0.17mm	0.03mm-0.02mm
Volume Weight	≤460G/L	±60G/L
Outside Dimension	25-100mm	±1mm
	100-15mm	≤±1%
Perpendicularity		≤1.0%(height)
Depth of parallelism		≤1.0%(height)
mesh number	200mesh, 300mesh, 400mesh

Physical and Chemical Properties:

Name		Unit	Index
Chemical Composition	Al2O3	%	35.1±1.6
	MgO	%	13.5±1.5
	SiO2	%	50.0±1.8
Compression Strength	A-axis	Mpa	≥15.0
	B-axis	Mpa	≥3.0
	C-axis	Mpa	≥0.15
Coefficient of Thermal Expansion (20-800ºC)		ºC	≤1.5*10-6
Soften temperature		ºC	≤1410
Thermal Shock Resistance		ºC	≤550ºC
Water-absorbing rate		%	24±4%
Cordierite Crystal Content		%	≥90
Open area		%	≥70%

Catalytic Principle:
Using the noble metal catalyst which coated on the carrier, catalyze the harmful gases such as HC, CO, NOx, etc. at a suitable temperature, to make the reaction between three kinds of harmful gases, the reaction equation is as follows:
2CO+O₂=CO₂
2C₂H₆+7O₂=CO₂+6H₂O
2NO+2CO=N₂+2CO₂